Turbinol X
|
|
|
|
|
|
|
|
透平能 X
|
|
|
|
|
|
|
|
|
|
|
|
32
|
46
|
68
|
32 XEP
|
46 XEP
|
|
颜色
|
ISO2049
|
-
|
<0.5
|
<0.5
|
<0.5
|
<0.5
|
<0.5
|
|
密度15 °C
|
ISO3675
|
kg/m3
|
849
|
860
|
870
|
852
|
860
|
|
运动粘度
|
ISO3105
|
mm2/s
|
|
|
|
|
|
|
|
@ 40 °C
|
|
32
|
46
|
68
|
32
|
46
|
|
|
@ 100 °C
|
|
5.7
|
7.1
|
8.8
|
5.7
|
7.1
|
|
粘度指数
|
ISO2909
|
-
|
112
|
112
|
106
|
112
|
112
|
|
闪点(COC)
|
ISO2592
|
°C
|
222
|
234
|
236
|
220
|
234
|
|
倾点
|
ASTM D97
|
°C
|
-15
|
-15
|
-12
|
-15
|
-15
|
|
中和值
|
ASTM D664
|
mgKOH/g
|
0.05
|
0.05
|
0.05
|
0.05
|
0.05
|
|
残碳量
|
ASTM D4530
|
%wt
|
<0.01
|
<0.01
|
<0.01
|
<0.01
|
<0.01
|
|
TOST 时间
|
ASTM D943
|
|
|
|
|
|
|
|
- TAN 2.0 mgKOH/g
|
|
hrs
|
>10,000
|
>10,000
|
>10,000
|
>10,000
|
>10,000
|
|
|
|
|
|
|
|
|
|
|
RBOT
|
ASTM D2272
|
min
|
810
|
870
|
-
|
700
|
700
|
|
-鼓氮后
|
|
min
|
805
|
750
|
-
|
664
|
670
|
|
空气释放性50 °C
|
ASTM D3427
|
min
|
<3
|
<3
|
<3
|
<3
|
<3
|
|
破乳化性
|
DIN51589/1
|
s
|
<100
|
<100
|
<100
|
<100
|
<100
|
|
消泡趋势/稳定性
|
ASTM D892
|
|
|
|
|
|
|
|
|
程序I: 25 °C
|
ml
|
30/0
|
<5/0
|
-
|
10/0
|
<5/0
|
|
|
程序ll: 95 °C
|
|
20/0
|
20/0
|
-
|
20/0
|
20/0
|
|
|
程序III: 25 °C
|
|
5/0
|
<5/0
|
-
|
<5/0
|
<5/0
|
|
抗腐、防锈性"A"
|
ISO7210
|
-
|
pass
|
pass
|
pass
|
pass
|
pass
|
|
"B"
|
ISO7210
|
-
|
pass
|
pass
|
pass
|
pass
|
pass
|
|
铜腐蚀性
|
ISO2160
|
-
|
1b
|
1b
|
1b
|
1b
|
1b
|
|
3h/100°C
|
|
|
|
|
|
|
|
|
四球磨损直径
|
|
|
|
|
|
|
|
|
40kg/1h/75°C/1200rpm
|
|
mm
|
0.58
|
-
|
-
|
0.47
|
0.46
|
|
40kg/1h/RT/1400rpm
|
|
mm
|
0.55
|
-
|
-
|
0.49
|
0.50
|
|
FZG A/8.3/90
|
IP334
|
Load
|
6
|
7
|
7
|
9
|
10
|
|
|
失效
|
|
|
|
|
|
|
|
以上数据为典型值，仅供参考
|
|
|
|
|
|
|
|